氧化钨 (WO3-x) 纳米粒子墨水

Avantama P-10 | Tungsten oxide nanoparticle dispersion | WO₃ ink | Tungsten oxide suspension | Nanograde P-10 | WO₃ dispersion

Tungsten oxide (WO3-x) nanoparticle ink

T487449-5ml

5ml

该WO3-x纳米粒子墨水可用于狭缝染料，旋转涂布和刮刀涂布，从而用作印刷电子器件中的空穴传输层。氧化钨纳米颗粒墨水是基于氧化钨（WO3）纳米颗粒在异丙醇中的胶体悬浮液的一种孔选择性界面层墨水。WO3颗粒的平均大小已优化为12-16nm左右。氧化钨纳米颗粒在亲水性和疏水性基体上具有较高的加工性能和易成层性。WO3-x纳米粒子墨水普遍适用于普通和倒置结构的太阳能电池。退火温度 应用 WO3纳米粒子墨水可以作为空穴提取层（HEL）材料应用于OPV电池中。氧化钨纳米粒子墨水可与PEDOT：PSS配方混合，以微调电子和形态干层特性（例如导电性、表面粗糙度或层孔隙率）。 This WO3-xnanoparticle ink is for slot-dye, spin-coating and doctor blading for the use as hole transport layer in printed electronics. Tungsten oxide nanoparticle ink is a hole-selective interface layer ink based on a colloidal suspension of tungsten oxide (WO3) nanoparticles in isopropanol. The average size of WO3particle is optimized around 12-16 nm. Tungsten oxide nanoparticle exhibits high work function, processability and easy layer formation on hydrophilic as well as hydrophobic substrates.This WO3-xnanoparticle ink is universally applicable in normal and inverted architecture solar cells.Annealing temperature

0.7992g/mL at 25°C

使用前：超声波和（可选）通过0.45 μm PTFE过滤器过滤工作条件：在氮气（或低湿度）下使用和薄膜干燥后处理：在80°C-120°C下对沉积的WO3-x薄膜进行退火

≤ 50 nm (BET)，浓度：2.5 wt. % in 2-propanol